Bone cement composition and method of making the same

ABSTRACT

Disclosed herein is a composition suitable for use in spinal surgery. The composition generally includes a reaction product or settable mixture of first and second components, the first component including a spray-dried inorganic filler, a radical donor, and a pre-polymerized vinyl polymer, and the second component including a radical scavenger, a diluent, a polymerization accelerator, and a reactive monomer. Furthermore, disclosed herein is a method of making the composition, which generally includes mixing the first and second components under conditions suitable to form a curable reaction product.

BACKGROUND OF THE DISCLOSURE

1. Field of the Disclosure

The disclosure generally relates to compositions useful as bone cements and, more specifically, to compositions useful in spinal surgery, a kit containing packaged components of the composition, and a method of making the composition.

2. Brief Description of Related Technology

Bone cement compositions are known to be useful in bonding or affixing an implant material to natural bone and to otherwise repair damaged natural bone. These compositions are especially useful in orthopedic and dental procedures. Although bone cement compositions enjoy wide use in the medicinal arts, these compositions need to be carefully designed depending on the surgical site at which they will be used. For example, compositions suitable for use in repairing a damaged bone in a limb may not be ideally suited for use in repairing damaged teeth. Similarly, compositions useful in repairing a limb or a tooth may not be ideally suited for surgically repairing the spinal column.

Spinal surgery is complex and risky given the proximity of the surgical site to the spinal cord and major organs. Conventional spinal surgery can repair fractured vertebrae and restore a patient's height, but it is highly invasive and involves significant risks. These surgeries involve making long incisions in the patient's chest or back so that metal instruments can move the fractured bones back into their normal positions. However, the instruments used in these surgeries are not optimally designed to manipulate deteriorated bone. The bones are then held in place by metal implants, which in the case of elderly patients with osteoporosis, can fail to hold due to the softness of the inner cancellous bone to which the implants are affixed or bonded. Consequently, conventional spinal surgery is performed in rare circumstances. Even when it is performed, the invasiveness of the procedure can result in damage to the spinal cord, pain, infection, and other disorders requiring post-operative, corrective procedures.

Recent developments in spinal surgery have made it possible to reduce the invasiveness prevalent in conventional procedures, thereby reducing some of the risks historically associated with the procedures. Among those developments are developments in compositions used to bond implants to natural bone or act as bone substitutes themselves. Another recent development is the ability to use syringe-like devices to deliver these compositions to the surgical site in a non-invasive manner. Suitable devices and delivery methods are disclosed in U.S. Pat. Nos. 6,241,734 and 6,613,054, and U.S. patent application Publication Nos. 2004/0122359 and 2002/0191487, the disclosures of which are incorporated herein by reference. In combination, conventional bone cement compositions along with the improved delivery methods these publications describe can reduce the invasiveness of conventional spinal surgery making the procedure a more viable option for patients in need of treatment.

Typically, current bone cement compositions are sold in two-part preparations containing a powder (or dry) part and a liquid (or wet) part, which, when combined, polymerize to form a hardened substance mimicking many of the physical properties of natural bone. The powder part includes a filler and a polymeric material, while the liquid part includes a reactive monomer (e.g., methylmethacrylate). The filler is a material that is bioactive on its surface to promote the natural growth of bone thereon. An example of such a filler is hydroxyapatite. Hydroxyapatite has a large surface area that undesirably absorbs the reactive monomer. Thus, the current preparations contain an excess amount of reactive monomer because a portion of the reactive monomer is absorbed into the hydroxyapatite and, therefore, does not participate in the polymerization reaction. When the two parts are combined to form the preparation and applied in practice, the monomer can undergo an exothermic reaction as the composition hardens. This heat generated by the reaction is highly undesirable because it can damage nerves, bones, and surrounding tissue, for example. This is especially undesirable in spinal surgery due to the proximity of the spinal cord. Additionally, the presence of the reactive monomer can result in undesired shrinkage of the composition after polymerization—diminishing bond quality between the composition and the bone to which the composition is bonded/applied. Moreover, the reactive monomer can be toxic to a patient if present in large amounts. Thus, the less the amount of reactive monomer necessary in the composition the less likely that the composition will experience undesired shrinkage, and the reduced incidences of patient exposure to heat and toxic materials.

Accordingly, there is a need for an improved bone cement composition including a reduced amount of reactive monomer, and a filler with a suitable surface area, particle size, and rheological properties for the intended use of the composition.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

Disclosed herein is a composition comprising a reaction product or a settable mixture of first and second components, the first component including a spray-dried inorganic filler, a radical donor, and a pre-polymerized vinyl polymer, and the second component including a radical scavenger, a diluent, a polymerization accelerator, and a reactive monomer. Also disclosed herein is a method of making the composition, which generally includes mixing the first and second components under conditions suitable to form the reaction product. The first component also can be referred to as a the dry or powder component as that is its usual physical state. Similarly, the second component also can be referred to as a wet or liquid component as that is its usual physical state. Also disclosed herein is a kit where the first and second components are maintained apart from each other (e.g., separately packaged or contained) until they are ready for use in forming the composition.

As described hereinafter, embodiments of the combination of ingredients comprising the first and second components advantageously provides a bone cement composition that overcomes deficiencies heretofore unaddressed in the field. Specifically, the first component includes a spray-dried inorganic filler. Suitable inorganic fillers include tricalcium phosphate, tetracalcium phosphate, hydroxyapatite, fluoride-substituted hydroxyapatite, strontium-substituted hydroxyapatite such as those disclosed in international publication WO 03/103734, the disclosure of which is incorporated herein by reference.

In one embodiment, the inorganic filler is spray-dried and can be prepared by mixing a commercially-available inorganic filler with an organic solvent to obtain a mixture that is then spray-dried using conventional spray-drying mechanisms and techniques to provide the spray-dried inorganic filler. Preferably, the spray-dried inorganic filler is a spray-dried hydroxyapatite and is prepared by mixing a commercially-available hydroxyapatite with an organic solvent to obtain a mixture, which is then spray-dried using conventional spray-drying mechanisms and techniques, resulting (with additional sintering) in a 60-fold reduction in surface area. Hydroxyapatite is commercially available from a variety of sources, such as, for example, Merck KGaA (Germany). Precipitated inorganic fillers, such as precipitated hydroxyapatite also can be spray-dried and used in the composition and in accordance with the disclosed method of making the composition.

The organic solvent can be any organic liquid that can be readily volatilized when spray-dried using conventional spray-drying mechanisms and techniques. Preferably, however, the organic solvent is selected from the group consisting of polyvinyl alcohol (PVA), polyvinyl pyrrolidine (PVP), acetone; alcohols, polyethylene glycol (PEG), oils of fatty acids, and mixtures thereof. Among the organic solvents, PVA is more highly preferred.

Next, the spray-dried inorganic filler should be sintered at a temperature of about 900° C. to about 1280° C. for about ten minutes per kilogram to about five hours per kilogram, preferably at a temperature of about 1200° C. to about 1240° C. for about 30 minutes per kilogram to about two hours per kilogram. The resultant, sintered and spray-dried inorganic filler can than be easily broken into smaller pieces to obtain a sintered, spray-dried inorganic filler having a preferred particle size falling within the range of particle size for the pre-polymerized vinyl polymer (i.e., about 20 micrometers (μm) to about 55 μm), described below. Additionally, because the components of the composition and the composition itself will likely have to traverse a narrow and possibly tortuous path through a syringe-like devices and/or other delivery mechanisms to the surgical site, it is desirable to utilize materials that will not clog the path. Consequently, the smaller the particle size, the less likely the material will clog this path.

The first component generally includes about 0.5 wt. % to about 99.5 wt. % of the spray-dried inorganic filler, based on the total weight of the first component. Preferably, the first component includes about 10 wt. % to about 70 wt. % of the filler, and even more preferably about 30 wt. % to about 50 wt. % of the filler, based on the total weight of the first component.

As noted above, the first component can also include a pre-polymerized vinyl polymer. Preferably, the pre-polymerized vinyl polymer is selected from the group consisting of poly(methyl methacrylate) (PMMA), prepolymerized styrene acrylates, poly-methacrylate, poly-ethacrylate, poly-butylmethacrylate, and copolymers thereof, and mixtures thereof. As noted above, preferably the pre-polymerized vinyl polymer comprises beads having an average particle size of about 20 μm to about 35 μm. Preferably, the pre-polymerized vinyl polymer is PMMA.

The first component generally includes about 0.5 wt. % to about 99.5 wt. % of the pre-polymerized vinyl polymer, based on the total weight of the first component. Preferably, the first component includes about 50 wt. % to about 90 wt. % of the pre-polymerized vinyl polymer, and even more preferably about 30 wt. % to about 70 wt. % of the pre-polymerized vinyl polymer, based on the total weight of the first component.

A radical donor also is present in the first component. As described in more detail below, the radical donor is used to initiate a polymerization reaction with the reactive monomer present in the second component. Preferably, the radical donor is selected from the group consisting of benzoyl peroxide (BPO), azo-bis-isobutyrylnitrile (AIBN), and mixtures thereof.

In one embodiment, the balance of the first component generally is made up of the radical donor. Thus, the first component can include about 0.5 wt. % to about 5 wt. % of the radical donor, based on the total weight of the spray-dried inorganic filler and the pre-polymerized vinyl polymer. Preferably, the first component includes about 0.6 wt. % to about 3 wt. % of the radical donor, and even more preferably about 0.9 wt. % to about 2 wt. % of the radical donor, based on the total weight of the spray-dried inorganic filler and the pre-polymerized vinyl polymer.

Optionally, the first component can include an ingredient selected from the group consisting of antibiotics, cytostatic agents, analgesic agents, disinfectants, preservatives, growth factors, proliferative factors, proteins, peptides, biopolymers, imageable markers, dyes, and mixtures thereof. Particularly preferred ingredients among the foregoing include those selected from the group consisting of gentamycine, trombamycine, clindamycine, vancomycine, β-TGF or an analog thereof, a bone morphogenic protein series compound, and mixtures thereof.

Suitable imageable markers include, but are not limited to, barium sulfate (BaSO₄), zirconium dioxide, CHI₃, Na₂FPO₃, and CaF₂. Among these markers, barium sulfate is preferred. If present, the imageable marker may comprise up to 30 wt. % of the first component. To the extent an imageable marker is present, it will reduce the amount of spray-dried inorganic filler present in the first component. The imageable marker is not a necessary component. Instead, its presence in the composition would assist a user (e.g., a surgeon) in visualizing the application of the composition to a surgical site via an image-readable device (e.g., a fluoroscope in the case of barium sulfate). The presence of the imageable marker, therefore, does not impart any mechanical attributes to the composition—it is merely an aid to assist the user.

Similarly, a dye, if present does not impart any mechanical attributes to the composition—it also is merely an aid to assist the user (e.g., surgeon, medical technician, aid, or nurse). For example, the dye could be used to readily inform the surgeon of the type of composition he/she is using. A purple-colored dye may have become known in the field by users to be indicative of a bone cement composition suitable for use in the spine, whereas a different color material may be known in the art by users to be indicative of a bone cement composition suitable for another application.

As described above, in one embodiment, the second component can include a polymerization accelerator, a reactive monomer, a diluent, and a radical scavenger. Preferably, the polymerization accelerator is selected such that the polymerization reaction occurs at or below normal body temperatures so as not to cause damage to the surgical site and surrounding areas. The polymerization accelerator preferably is a tertiary amine. Suitable tertiary amines include, but are not limited to, dimethylparatoluidine (DMPT) and dihydroxyethylorthotoluidine. Although, DMPT is believed to be toxic to humans, in low concentrations, it may still be used without adverse consequences.

The second component generally includes about 0.1 wt. % to about 3 wt. % of the polymerization accelerator, based on the total weight of second component. Preferably, the second component includes about 0.2 wt. % to about 2 wt. % of the polymerization accelerator, and even more preferably about 0.3 wt. % to about 0.4 wt. % of the polymerization accelerator, based on the total weight of the second component.

A reactive monomer also is present in the second component. The reactive monomer is selected from the group consisting of methyl methacrylate (MMA), PEG monoacrylates, PEG diacrylates, PEG monomethacrylates, PEG dimethacrylates, PEG-mono/di-acrylate/methacrylate, butanediol methacrylates, polyolefin-acrylates, urethaneacrylates, methacrylates, and mixtures thereof. Among the PEG-based reactive monomers, those having a molecular weight in a range of about 200 Daltons (D) to about 1500 D are preferred. Preferably, the reactive monomer is MMA.

The second component generally include about 10 wt. % to about 99 wt. % of the reactive monomer, based on the total weight of the second component. Preferably, the second component includes about 40 wt. % to about 95 wt. % of the reactive monomer, and even more preferably about 60 wt. % to about 90 wt. % of the reactive monomer, based on the total weight of the second component.

In one embodiment, the second component can also include a diluent. Suitable diluents include, but are not limited to, polyethylene glycol (PEG), an ester of mellitic acid, and mixtures thereof. Preferably, the diluent is PEG. When present, a preferred ester of mellitic acid is tri-octylmellitic ester. Generally, the diluent should have a molecular weight such that the diluent remains in liquid form at room temperature. When PEG is used, preferably its molecular weight is about 100 D to about 1000 D, and more preferably about 400 D to about 800 D. The presence of the diluent in the second component provides multiple benefits. For example, the diluent desirably provides the ability to control the stiffness of the bone cement composition after curing/hardening. While not wishing to be bound by any particular theory, it is believed that lower stiffness is beneficial because it better simulates the actual properties of human bones. The presence of PEG in the aforementioned weight range does not adversely affect the compressive strength and bending strength of the preparation. Thus, the stiffness can be more readily/easily controlled by the presence of PEG, without compromising the compressive and bending strengths of the preparation relative to the prior art preparations. The compressive and bending strengths may be adversely affected when the amount of diluent exceeds 30 wt. %, based on the total weight of the composition. Furthermore, the presence of diluent rapidly destabilizes the radical donor (thus, resulting in a faster hardening of the preparation) and reduces the amount of polymerization accelerator (e.g., DMPT) necessary. If the compression strength of the hardened preparation can be lowered from 30 mega-Pascals (mPa), then the amount of diluent (e.g., PEG) can be increased with a concomitant decrease in the amount of reactive monomer.

The second component generally includes about 1 wt. % to about 90 wt. % of the diluent, based on the total weight of the second component. Preferably, the second component includes about 5 wt. % to about 60 wt. % of the diluent, and even more preferably about 10 wt. % to about 40 wt. % of the diluent, based on the total weight of the second component.

In one embodiment, the second component can also include a radical scavenger. The radical scavenger is present in the second component to retard or arrest the ability of the reactive monomer to self polymerize (self-polymerization is undesirable). The reactive monomer is often sold with sufficient radical scavenger. Preferably, the radical scavenger is selected from the group consisting of hydroquinone, hydroquinone monomethylether, vitamin E, and mixtures thereof.

The amount of the radical scavenger present in the second component generally will depend upon the amount of reactive monomer present. To the extent that additional amounts of radical scavenger are needed/desired, it may be added such that the second component includes about 5 parts per million (ppm) to about 500 ppm of the radical scavenger. Preferably, the radical scavenger is present in the second component in an amount of about 30 ppm to about 400 ppm, and even more preferably about 50 ppm to about 200 ppm.

Optional ingredients present in the second component can include one or more selected from the group consisting of a dye, an admixture of proteins, a chemotherapeutic, a drug, an antibiotic, and mixtures thereof. The admixture of proteins can be an admixture of heat sensitive/unsensitive proteins, which can include mitogenic growth factors, morphogenic growth factors, and mixtures thereof. An example of a suitable drug that can be part of the second component is bisphosphonate. Although the second component can include an antibiotic, preferably the antibiotics when present in the composition are present in the first component.

The bone cement composition is generally prepared by a method that generally includes mixing the first and second components under conditions suitable to form the reaction product. The reaction product preferably is curable under standard pressure (i.e., one bar) and at temperatures ranging from standard temperature (i.e., 25° C.) to about 50° C. The weight ratio of first (dry or powder) component to the second (wet or liquid) component is about 2.2:1 to about 3.3:1, preferably 2.5:1. For example, if the preparation includes ten grams of the first component, then it should include about four grams of the second component.

When the first and second components are combined, a polymerization reaction is initiated by the polymerization accelerator present in the second component and the radical donor present in the first component. In practice, the radical donor will decompose when it encounters the polymerization accelerator evolving a free radical that will attack the double bonds present in the monomer causing the monomer to polymerize and ultimately harden. This reaction in the context of the composition will yield a cured composition

In preferred embodiments, the components of the composition are capable of being readily injectable through a syringe-like device or other delivery mechanism to a surgical site, where they react to form the composition and cure to a hardened state. The composition is persistent at the surgical site, preferably adhering to the tissue and/or bone at the site. Furthermore, the composition is stable in that it generally undergoes no significant changes in situ. When set/cured, the composition is also tough and elastic in that it is capable of bearing loads without experiencing undue or permanent deformation. Still further, the composition is believed to be well-tolerated by the body in that it produces, at most, tolerable levels of immune and inflammatory responses. It is to be appreciated, however, that preferred embodiments of the composition, while satisfying at least some of these advantages, may not satisfy all of these advantages in every instance.

In one embodiment, the composition preferably is sold/distributed to users in a kit where the first and second components are maintained apart (e.g., separately packaged or contained) until they are ready for use in forming the composition. The user may receive a mixer apparatus containing the components in separate compartments thereof. See generally, U.S. Pat. No. 6,241,734 and U.S. patent application publication Nos. 2004/0122359 A1 and 2002/0191487 A1, the disclosures of which are incorporated herein by reference. These publications generally describe suitable apparatus for mixing and delivering the composition's components and mixtures thereof to form the composition. The components likely will be mixed by the user immediately prior to the surgical procedure with a suitable mixing apparatus. Once the composition is formed, it should be transferred to an apparatus suitable to deliver the composition (or mixture of components) to the surgical site before the composition (or mixture) sets/cures.

The composition may be applied using a variety of mechanisms such as, for example, those described in U.S. Pat. Nos. 5,972,015 and 6,066,154, the disclosures of which are incorporated herein by reference. These patents generally describe a procedure referred to as “Kyphoplasty,” which uses one or two balloons, similar to angioplasty balloons, to reduce the vertebrae bone fracture and restore vertebral height prior to injecting a bone cement composition. For example, two balloons are introduced into the vertebra via bilateral transpedicular cannulae. The balloons are inflated to reduce the fracture, then deflated and removed, leaving a relatively empty cavity into which a bone cement composition is injected. The inflation of the balloons and subsequent injection of the composition helps restore vertebral height.

EXAMPLE

The following example is provided to illustrate an embodiment of the disclosed composition, how it is made, and the results of tests performed on the composition, but is not intended to limit the scope of the disclosure.

Hydroxyapatite was obtained from Merck KGaA (Germany) and was spray-dried by Pharmarone (Germany) and then sintered to provide a sintered, spray-dried hydroxyapatite having a particle size of about 20 μm to about 35 μm. The surface area of the spray-dried and sintered hydroxyapatite was 0.8 m²/g, as determined by BET analysis. A first component (i.e., a dry or powder component) was prepared by combining (a) 7 grams of BPO obtained from Sigma Chemical Company, (b) 120 grams of Plexidon MW 422, which is a prepolymerized vinyl polymer, from Fa. Röhm GmbH (Darmstadt, Germany), (c) 156 grams of sintered, spray-dried hydroxyapatite, and (d) 31.2 grams of barium sulfate. These ingredients are mixed together in a ball mill rotating at a speed of 200 rotations per minute with 405 grams of Steatit balls of 20 mm diameter for 50 minutes. A second component (i.e., the wet or liquid component) was prepared and included (a) 64.6 grams MMA, (b) 5 grams butanediol-dimethacrylate, (c) 30 grams PEG (molecular weight of 400 D), and (d) 0.4 grams DMPT. Ten grams of the first component and 3.5 grams of the second components were mixed together at standard temperature and pressure and were set to provide a hardened material. The handling characteristics were measured at 19.5° C. The dough-time syringe was six minutes 20 seconds, the dough-time bone filler device was seven minutes 20 seconds, and the end dough-time was fifteen minutes.

The material then underwent strength tests. Specifically, the material was subjected to test performed in accordance with ISO 5833 to provide data regarding compressive and bonding strengths. The material had a compressive strength of 30.25 Newtons per square millimeter (N/mm²) measured after two hours, and 30.78 N/mm² measured after 24 hours. The material had a three-point bending strength of 25.6 MPa after 24 hours and dry incubation, and 37.2 MPa after three days immersion in saline at 37° C. The material had a Young's modulus (elastic modulus) of 1181 MPa after 24 hours dry incubation, and 1532 MPa after three days immersion in saline at 37° C.

The foregoing description is given for clearness of understanding only, and no unnecessary limitations should be understood therefrom, as modifications may be apparent to those having ordinary skill in the art. 

1. A composition comprising a reaction product of: (a) a first component comprising a spray-dried inorganic filler, a radical donor, and a pre-polymerized vinyl polymer; and, (b) a second component comprising a radical scavenger, a diluent, a polymerization accelerator, and a reactive monomer.
 2. The composition of claim 1, wherein the first component and second component are present in a weight ratio of about 2.2:1 to about 3.3:1.
 3. The composition of claim 1, wherein the first component further comprises an optional ingredient selected from the group consisting of an antibiotic, a cytostatic agent, an analgesic agent, a disinfectant, a preservative, a growth factor, a proliferative factor, a protein, a peptide, a biopolymer, an imageable marker, a dye, and mixtures thereof.
 4. The composition of claim 2, wherein the imageable marker is selected from the group consisting of barium sulfate (BaSO₄), zirconium dioxide, CHI₃, Na₂FPO₃, and CaF_(2,), and mixtures thereof.
 5. The composition of claim 1, wherein,the second component further comprises an optional ingredient selected from the group consisting of a dye, an admixture of proteins, a chemotherapeutic, a drug, an antibiotic, and mixtures thereof.
 6. The composition of claim 5, wherein the admixture of proteins is selected from the group consisting of mitogenic growth factors, morphogenic growth factors, and mixtures thereof.
 7. The composition of claim 5, wherein the drug is a bisphosphonate.
 8. The composition of claim 1, wherein the spray-dried inorganic filler comprises a sintered, spray-dried inorganic filler.
 9. The composition of claim 1, wherein the spray-dried inorganic filler is spray-dried hydroxyapatite.
 10. The composition of claim 9, wherein the spray-dried, modified hydroxyapatite is sintered, spray-dried hydroxyapatite.
 11. The composition of claim 1, wherein the radical donor is selected from the group consisting of benzoyl peroxide (BPO), azo-bis-isobutyrylnitrile (AIBN), and mixtures thereof.
 12. The composition of claim 1, wherein the pre-polymerized vinyl polymer is selected from the group consisting of poly(methyl methacrylate) (PMMA), prepolymerized styrene acrylates, poly-methacrylate, poly-ethacrylate, poly-butylmethacrylate, and copolymers thereof, and mixtures thereof.
 13. The composition of claim 12, wherein the pre-polymerized vinyl polymer is PMMA.
 14. The composition of claim 12, wherein the pre-polymerized vinyl polymer comprises beads having an average particle size of about 20 micrometers (μm) to about 55 μm.
 15. The composition of claim 1, wherein the radical scavenger is selected from the group consisting of hydroquinone, hydroquinone monomethylether, vitamin E, and mixtures thereof.
 16. The composition of claim 1, wherein the diluent is selected from the group consisting of polyethylene glycol (PEG), an ester of mellitic acid, and mixtures thereof.
 17. The composition of claim 16, wherein the ester of mellitic acid is tri-octylmellitic ester.
 18. The composition of claim 16, wherein the diluent has a molecular weight such that the diluent is a liquid at standard temperature and pressure.
 19. The composition of claim 16, wherein the PEG has a molecular weight of about 100 to about
 1000. 20. The composition of claim 19, wherein the PEG has a molecular weight of about 400 to about
 800. 21. The composition of claim 1, wherein the reactive monomer is selected from the group consisting of methyl methacrylate (MMA), PEG monoacrylates, PEG diacrylates, PEG monomethacrylates, PEG dimethacrylates, PEG-mono/di-acrylate/methacrylate, butanediol methacrylates, polyolefin-acrylates, urethaneacrylates, methacrylates, and mixtures thereof.
 22. The composition of claim 21, wherein the reactive monomer is MMA.
 23. The composition of claim 21, wherein the PEG monoacrylates, PEG diacrylates, PEG monomethacrylates, PEG dimethacrylates have a molecular weight in a range of about 200 Daltons (D) to about 1500 D.
 24. The composition of claim 1, wherein the polymerization accelerator is selected from the group consisting of dimethyl aniline, diethyl aniline, dimethylparatoluidine (DMPT), diethylparatoluidine, and mixtures thereof.
 25. The composition of claim 24, wherein the polymerization accelerator is selected from the group consisting of dimethylparatoluidine (DMPT) and dihydroxyethylorthotoluidine, and mixtures thereof.
 26. The composition of claim 25, wherein the polymerization accelerator is DMPT.
 27. The composition of claim 1, wherein the first component comprises about 0.5 wt. % to about 99.5 wt. % of the spray-dried inorganic filler, based on the total weight of the first component.
 28. The composition of claim 1, wherein the first component comprises about 0.5 wt. % to about 5 wt. % of a radical donor, based on the total weight of the spray-dried inorganic filler and the pre-polymerized vinyl polymer.
 29. The composition of claim 1, wherein the first component comprises about 0.5 wt. % to about 99.5 wt. % of pre-polymerized vinyl polymer, based on the total weight of the first component.
 30. The composition of claim 2, wherein the imageable marker is present in the first component and comprises up to about 30 wt. % of the first component, based on the total weight of the first component.
 31. The composition of claim 1, wherein the radical scavenger comprises about 5 parts per million parts of the second component (ppm) to about 500 ppm.
 32. The composition of claim 1, wherein the second component comprises about 1 wt. % to about 90 wt. % of the diluent, based on the total weight of the second component.
 33. The composition of claim 1, wherein second component comprises about 0.1 wt. % to about 3 wt. % of the polymerization accelerator, based on the total weight of the second component.
 34. The composition of claim 1, wherein the second component comprises about 10 wt. % to about 99 wt. % of reactive monomer, based on the total weight of the second component.
 35. A composition comprising a settable mixture of: (a) a first component comprising a spray-dried inorganic filler, a radical donor, and a pre-polymerized vinyl polymer; (b) a second component reactive with the first component, the second component comprising a radical scavenger, a diluent, a polymerization accelerator, and, a reactive monomer.
 36. A method of making a bone cement composition, the method comprising mixing (a) a first component comprising a spray-dried inorganic filler, a radical donor, and a pre-polymerized vinyl polymer; and (b) a second component comprising a radical scavenger, a diluent, a polymerization accelerator, and a reactive monomer, under conditions suitable to form a curable reaction product.
 37. The method of claim 37, further comprising curing the reaction product.
 38. The method of claim 37, further comprising mixing the first and second components in a weight ratio of the first component to the second component of about 1:3 to about 1:2.
 39. The method of claim 36, wherein the spray-dried inorganic filler comprises a sintered, spray-dried inorganic filler prepared by combining an inorganic filler with an organic solvent to form a mixture, spray drying the mixture, and sintering the spray-dried mixture.
 40. A kit comprising (a) a packaged first component comprising a spray-dried inorganic filler, a radical donor, and a pre-polymerized vinyl polymer; and, (b) a packaged second component comprising a radical scavenger, a diluent, a polymerization accelerator, and a reactive monomer.
 41. The kit of claim 40 further comprising an apparatus suitable to mix the first and second components.
 42. The kit of claim 40 further comprising an apparatus suitable to deliver a mixture of the first and second components to a surgical site. 